dc.description.abstractDespite having world record efficiencies, high costs associated with deposition and the substrate have barred III-V entry into terrestrial PV markets. Substrate reuse technology offers a promising route towards reducing III-V manufacturing costs where devices deposited on the substrate are lifted off to enable the substrate to be used for future growths. Controlled spalling is a potential substrate reuse method and is the focus of this work. Controlled spalling is a method of exfoliating single-crystal sheets by propagating a crack parallel to the surface by applying an external force to a sub-critically stressed overlayer deposited on the substrate. This work develops a method to reliably spall 2” (100)-Ge wafers in order to test the hypothesis that, despite having different geometries, the electroplating parameters used to controllably spall square test samples can be directly applied to the wafer-scale. An automated spalling jig is developed to enable safe wafer handling and facilitate controlled spalling at a constant velocity. Crack initiation is found to be a vital step to achieve controlled spalling at the wafer-scale. As-spalled (100)-Ge wafers are also investigated as substrates for III-V device growth. A 12.8% efficient single-junction GaAs device without an antireflective coating is grown on an as-spalled (100)-Ge wafer using HVPE at NREL. Spall depth for full wafers is observed to be inconsistent. Crack arrest lines that are generated during controlled spalling are amplified by defects that form during the electroplating process. However, arrest lines in Ge appear to be morphological defects only, as dislocations are not observed to form as a result of electroplating or controlled spalling processes.
dc.format.mediumborn digital
dc.format.mediummasters theses
dc.languageEnglish
dc.language.isoeng
dc.publisherColorado School of Mines. Arthur Lakes Library
dc.rightsCopyright of the original work is retained by the author.
dc.subjectcontrolled spalling
dc.subjectspalling
dc.subject(100)-germanium
dc.subjectsubstrate reuse
dc.subjectIII-V photovoltaics
dc.titleWafer-scale controlled spalling and reuse of (100)-oriented germanium
dc.typeText
dc.contributor.committeememberReimanis, Ivar E. (Ivar Edmund)
dc.contributor.committeememberTucker, Garritt J.
thesis.degree.nameMaster of Science (M.S.)
thesis.degree.levelMasters
thesis.degree.disciplineMetallurgical and Materials Engineering
thesis.degree.grantorColorado School of Mines


Files in this item

Thumbnail
Name:
Ley_mines_0052N_11778.pdf
Size:
3.075Mb
Format:
PDF

This item appears in the following Collection(s)

Show simple item record